ASTM C 920 : 2018
Current
The latest, up-to-date edition.
Standard Specification for Elastomeric Joint Sealants
Hardcopy , PDF
English
01-01-2018
Important note : All end users must be registered with an Account prior to user licenses being assigned.| Committee |
C 24
|
| DocumentType |
Standard
|
| Pages |
4
|
| PublisherName |
American Society for Testing and Materials
|
| Status |
Current
|
| Supersedes |
1.1This ASTM specification covers the properties of a cured single- or multicomponent cold-applied elastomeric joint sealant for sealing, caulking, or glazing operations on buildings, plazas, and decks for vehicular or pedestrian use, and types of construction other than highway and airfield pavements and bridges.
1.2A sealant meeting the requirements of this specification shall be designated by the manufacturer to be one or more of the types, classes, grades, and uses defined in Section 7.
1.3The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.4This standard is similar, but not identical, to ISO 11600 and ISO 11618.
1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
| ASTM C 1193 : 2011 : REV A | Standard Guide for Use of Joint Sealants |
| ASTM C 794 : 2018 | Standard Test Method for Adhesion-in-Peel of Elastomeric Joint Sealants |
| ASTM C 1193 : 2016 : R2023 | Standard Guide for Use of Joint Sealants |
| ASTM C 719 : 2022 | Standard Test Method for Adhesion and Cohesion of Elastomeric Joint Sealants Under Cyclic Movement (Hockman Cycle) |
| ASTM C 1442 : 2011 | Standard Practice for Conducting Tests on Sealants Using Artificial Weathering Apparatus |
| ASTM C 1246 : 2000 : R2012 | Standard Test Method for Effects of Heat Aging on Weight Loss, Cracking, and Chalking of Elastomeric Sealants After Cure |
| ASTM C 1193 : 2016 | Standard Guide for Use of Joint Sealants |
| ASTM C 661 : 2015 : R2022 | Standard Test Method for Indentation Hardness of Elastomeric-Type Sealants by Means of a Durometer |
| ASTM C 1183 : 1991 : R1997 | Standard Test Method for Extrusion Rate of Elastomeric Sealants |
| ASTM C 1193 : 2005 : REV A | Standard Guide for Use of Joint Sealants |
| ASTM C 717 : 2019 | Standard Terminology of Building Seals and Sealants |
| ASTM C 661 : 2015 | Standard Test Method for Indentation Hardness of Elastomeric-Type Sealants by Means of a Durometer |
| ASTM C 1193 : 2012 | Standard Guide for Use of Joint Sealants |
| ASTM C 1442 : 2014 : R2021 | Standard Practice for Conducting Tests on Sealants Using Artificial Weathering Apparatus |
| ASTM C 1247 : 2014 | Standard Test Method for Durability of Sealants Exposed to Continuous Immersion in Liquids |
| ASTM C 1247 : 2009 | Standard Test Method for Durability of Sealants Exposed to Continuous Immersion in Liquids |
| ASTM C 1193 : 2005 | Standard Guide for Use of Joint Sealants |
| ASTM C 1442 : 2014 | Standard Practice for Conducting Tests on Sealants Using Artificial Weathering Apparatus |
| ASTM C 1246 : 2017 | Standard Test Method for Effects of Heat Aging on Weight Loss, Cracking, and Chalking of Elastomeric Sealants After Cure |
| ASTM C 1247 : 1998 | Standard Test Method for Durability of Sealants Exposed to Continuous Immersion in Liquids |
| ASTM C 1246 : 2017 : R2022 | Standard Test Method for Effects of Heat Aging on Weight Loss, Cracking, and Chalking of Elastomeric Sealants After Cure |
| ASTM C 1442 : 2006 | Standard Practice for Conducting Tests on Sealants Using Artificial Weathering Apparatus |
| ASTM C 794 : 2018 : R2022 | Standard Test Method for Adhesion-in-Peel of Elastomeric Joint Sealants |
| ASTM C 1183 : 2004 | Standard Test Method for Extrusion Rate of Elastomeric Sealants |
| ASTM C 1183 : 2004 : R2008 | Standard Test Method for Extrusion Rate of Elastomeric Sealants |
| ASTM C 719 : 2014 : R2019 | Standard Test Method for Adhesion and Cohesion of Elastomeric Joint Sealants Under Cyclic Movement (Hockman Cycle) |
| ASTM C 1193 : 2000 | Standard Guide for Use of Joint Sealants |
| ASTM C 679 : 2015 : R2022 | Standard Test Method for Tack-Free Time of Elastomeric Sealants |
| ASTM C 1442 : 2003 | Standard Practice for Conducting Tests on Sealants Using Artificial Weathering Apparatus |
| ASTM C 793 : 2023 | Standard Test Method for Effects of Laboratory Accelerated Weathering on Elastomeric Joint Sealants |
| ASTM C 1247 : 2020 | Standard Test Method for Durability of Sealants Exposed to Continuous Immersion in Liquids |
| ASTM C 717 : 2024 | Standard Terminology of Building Seals and Sealants |
| ASTM C 510 : 2016 | Standard Test Method for Staining and Color Change of Single- or Multicomponent Joint Sealants |
| ASTM C 679 : 2015 | Standard Test Method for Tack-Free Time of Elastomeric Sealants |
| ASTM C 1193 : 2011 | Standard Guide for Use of Joint Sealants |
| ASTM C 510 : 2016 : R2022 | Standard Test Method for Staining and Color Change of Single- or Multicomponent Joint Sealants |
| ASTM C 793 : 2005 : R2017 | Standard Test Method for Effects of Laboratory Accelerated Weathering on Elastomeric Joint Sealants |
| ASTM C 1442 : 1999 | Standard Practice for Conducting Tests on Sealants Using Artificial Weathering Apparatus |
| ASTM C 1246 : 2000 | Standard Test Method for Effects of Heat Aging on Weight Loss, Cracking, and Chalking of Elastomeric Sealants After Cure |
| ASTM C 1246 : 2000 : R2006 | Standard Test Method for Effects of Heat Aging on Weight Loss, Cracking, and Chalking of Elastomeric Sealants After Cure |
| ASTM C 1193 : 2013 | Standard Guide for Use of Joint Sealants |
| ASTM C 1193 : 2009 | Standard Guide for Use of Joint Sealants |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.