ASTM E 3184 : 2024

1.1These digital reference images illustrate various categories, types and severity levels of discontinuities occurring in high-strength copper-base, nickel-copper, and related alloy castings. The digital reference images are an adjunct to this document and must be purchased separately from ASTM International if needed (see 2.4). Categories and severity levels for each discontinuity type represented by these digital reference images are described in 1.2.

1.2These reference images consist of forty-five 5 in. by 7 in. (127 mm by 178 mm) nominal size reproductions (twenty made from 1 in. (25.4 mm) plate castings exposed with low voltage X rays for thicknesses up to and including 2 in.) and twenty-five made from 3 in. (76 mm) plate castings exposed with 2 MV X rays or Cobalt 60 isotope for thicknesses greater than 2 in. up to and including 6 in. Unless otherwise specified in a purchaser supplier agreement (see 1.1), each discontinuity category is for comparison only with production digital images produced with radiation energy levels within the thickness range addressed by the category. These digital reference images illustrate discontinuities in sand-cast manganese-nickel-aluminum bronze-alloy plates and are representative of those found in narrow freezing range (formerly “high shrinkage”) high-strength copper and nickel-copper alloys. The categories, types and severity levels for the adjunct digital reference images of this standard are shown in 1.2.1 – 1.2.3 (see Note 2):

1.3All areas of this standard may be subject to agreement between the cognizant engineering organization and the supplier, or specific direction from the cognizant engineering organization. These items should be addressed in the purchase order or the contract.

1.4These digital reference images are not intended to illustrate the types and degrees of discontinuities found in high-strength copper-base, nickel-copper, and related alloy castings when performing film radiography. If performing film radiography of high-strength copper-base, nickel-copper, and related alloy castings, refer to Reference Radiographs E272.

1.5Only licensed copies of the software and images shall be utilized for production examination. A copy of the ASTM/User license agreement shall be kept on file for audit purposes (see Note 3).

1.6The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.7This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.8This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.