ASTM E 353 : 2014 : REDLINE
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Test Methods for Chemical Analysis of Stainless, Heat-Resisting, Maraging, and Other Similar Chromium-Nickel-Iron Alloys
14-08-2020
English
15-09-2014
CONTAINED IN VOL. 03.05, 2015 Describes the chemical analysis of stainless, heat-resisting, maraging, and other similar chromium-nickel-iron alloys having chemical compositions within the specified limits.
Committee |
E 01
|
DocumentType |
Redline
|
Pages |
64
|
PublisherName |
American Society for Testing and Materials
|
Status |
Superseded
|
SupersededBy |
1.1These test methods cover the chemical analysis of stainless, heat-resisting, maraging, and other similar chromium-nickel-iron alloys having chemical compositions within the following limits:
Element | Composition Range, % | |||
Aluminum | 0.002 | to 5.50 | ||
Boron | 0.001 | to 0.20 | ||
Carbon | 0.01 | to 1.50 | ||
Chromium | 0.01 | to 35.00 | ||
Cobalt | 0.01 | to 15.00 | ||
Niobium | 0.01 | to 4.00 | ||
Copper | 0.01 | to 5.00 | ||
Lead | 0.001 | to 0.50 | ||
Manganese | 0.01 | to 20.00 | ||
Molybdenum | 0.01 | to 7.00 | ||
Nickel | 0.01 | to 48.00 | ||
Nitrogen | 0.001 | to 0.50 | ||
Phosphorus | 0.002 | to 0.35 | ||
Selenium | 0.01 | to 0.50 | ||
Silicon | 0.01 | to 4.00 | ||
Sulfur | 0.002 | to 0.50 | ||
Tantalum | 0.01 | to 0.80 | ||
Tin | 0.001 | to 0.05 | ||
Titanium | 0.01 | to 4.50 | ||
Tungsten | 0.01 | to 4.50 | ||
Vanadium | 0.005 | to 1.00 | ||
Zirconium | 0.001 | to 0.20 |
1.2The test methods in this standard are contained in the sections indicated below:
Sections | |
Aluminum, Total, by the 8-Quinolinol Gravimetric Method (0.20 % to 7.00 %) | 119 |
Aluminum, Total, by the 8-Quinolinol Spectrophotometric Method (0.003 % to 0.20 %) | 71 |
Carbon, Total, by the Combustion–Thermal Conductivity Method | Discontinued |
Carbon, Total, by the Combustion Gravimetric Method (0.05 % to 1.50 %) | Discontinued |
Chromium by the Atomic Absorption Method (0.006 % to 1.00 %) | 202 |
Chromium by the Peroxydisulfate Oxidation–Titration Method (0.10 % to 35.00 %) | 212 |
Chromium by the Peroxydisulfate-Oxidation Titrimetric Method | Discontinued |
Cobalt by the Ion-Exchange–Potentiometric Titration Method (2 % to 15 %) | 53 |
Cobalt by the Nitroso-R-Salt Spectrophotometric Method (0.01 % to 5.0 %) | 61 |
Copper by the Neocuproine Spectrophotometric Method (0.01 % to 5.00) %) | 109 |
Copper by the Sulfide Precipitation-Electrodeposition Gravimetric Method (0.01 % to 5.00 %) | 82 |
Lead by the Ion-Exchange-Atomic Absorption Method (0.001 % to 0.50 %) | 127 |
Manganese by the Periodate Spectrophotometric Method (0.01 % to 5.00 %) | 8 |
Molybdenum by the Ion Exchange–8-Hydroxyquinoline Gravimetric Method | 242 |
Molybdenum by the Spectrophotometric Method (0.01 % to 1.50 %) | 190 |
Nickel by the Dimethylglyoxime Gravimetric Method (0.1 % to 48.0 %) | 172 |
Phosphorus by the Alkalimetric Method (0.02 % to 0.35 %) | 164 |
Phosphorus by the Molybdenum Blue Spectrophotometric Method (0.002 % to 0.35 %) | 18 |
Silicon by the Gravimetric Method (0.05 % to 4.00 %) | 46 |
Sulfur by the Gravimetric Method | Discontinued |
Sulfur by the Combustion-Iodate Titration Method (0.005 % to 0.5 %) | Discontinued |
Sulfur by the Chromatographic Gravimetric Method | Discontinued |
Tin by the Solvent Extraction–Atomic Absorption Method (0.002 % to 0.10 %) | 180 |
Tin by the Sulfide-Iodometric Titration Method (0.01 % to 0.05 %) | 90 |
Titanium, Total, by the Diantipyrylmethane Spectrophotometric Method (0.01 % to 0.35 %) | 231 |
Vanadium by the Atomic Absorption Method (0.006 % to 0.15 %) | 221 |
1.3Test methods for the determination of carbon and sulfur not included in this standard can be found in Test Methods E1019.
1.4Some of the composition ranges given in 1.1 are too broad to be covered by a single test method and therefore this standard contains multiple test methods for some elements. The user must select the proper test method by matching the information given in the Scope and Interference sections of each method with the composition of the alloy to be analyzed.
1.5The values stated in SI units are to be regarded as standard.
1.6This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Specific hazards statements are given in Section 6 and in special “Warning” paragraphs throughout these test methods.
AWS A5.4 : 92(R2000) | STAINLESS STEEL ELECTRODES FOR SHIELDED METAL ARC WELDING, SPECIFICATION FOR |
SAE AMS 5349 : 2013 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 13CR, FREE MACHINING; HARDENED AND TEMPERED |
SAE AS7245:2012 | INSERTS, SCREW THREAD, HELICAL COIL 19CR-9.2NI, CORROSION RESISTANT STEEL, PROCUREMENT SPECIFICATION FOR |
SAE AMS 5697 : 2018 | STEEL, CORROSION-RESISTANT, WIRE, 19CR - 9.5NI (304), SOLUTION HEAT TREATED |
SAE AMS 5900 : 2000 | STEEL BARS, FORGINGS, AND TUBING, CORROSION RESISTANT, 14CR - 2.1MO - 0.30CB - 1.0V (1.05 - 1.15C), PREMIUM AIRCRAFT QUALITY FOR BEARING APPLICATIONS, DOUBLE VACUUM MELTED |
SAE AMS 5346 : 2014 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 15CR - 4.6NI - 0.22CB (NB) - 2.8CU, SOLUTION AND PRECIPITATION HEAT TREATED (H925), 180 KSI (1241 MPA) TENSILE STRENGTH (15-5) |
SAE AMS 5866 : 2016 | STEEL, CORROSION-RESISTANT, FLAT WIRE, 18CR - 9.0NI (302), SPRING TEMPER |
SAE AMS 5784 : 2011 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE 29CR - 9.5NI |
SAE AMS 5737 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS AND TUBING, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED, 1650 DEGREES F (899 DEGREES C), SOLUTION AND PRECIPITATION HEAT TREATED |
SAE AMS 5864 : 2013 | STEEL, CORROSION-RESISTANT, PLATE 13CR - 8.0NI - 2.2MO - 1.1AL VACUUM INDUCTION PLUS CONSUMABLE ELECTRODE MELTED SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5612 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 12CR, FERRITE CONTROLLED, ANNEALED |
SAE AMS 5546 : 1990(S2017) | STEEL SHEET AND STRIP, CORROSION AND MODERATE HEAT RESISTANT 16.5CR - 4.5NI - 2.9MO - 0.10N COLD ROLLED, TEMPERED |
ASTM F 1376 : 1992 : R1999 | Standard Guide for Metallurgical Analysis for Gas Distribution System Components |
SAE AMS 5935 : 2016 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 12CR - 10NI - 2MO - 0.9AL - 0.3TI, VACUUM INDUCTION PLUS VACUUM CONSUMABLE ELECTRODE MELTED SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5575 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, WELDED TUBING, 18CR - 10.5NI - 0.70CB (NB) (347), SOLUTION HEAT TREATED |
SAE AMS 5902 : 2008 | STEEL, CORROSION-RESISTANT, SHEET AND STRIP, 18CR - 8NI (SAE 30301), COLD ROLLED, 3/4 HARD, 175 KSI (1207 MPA) TENSILE STRENGTH |
NACE TM 04 98 : 2014 | EVALUATION OF THE CARBURIZATION OF ALLOY TUBES USED FOR ETHYLENE MANUFACTURE |
SAE ARP 4926 : 2011 | ALLOY VERIFICATION AND CHEMICAL COMPOSITION INSPECTION OF WELDING WIRE |
MIL-S-24149 Revision C:1989 | STUDS, WELDING AND ARC SHIELDS (FERRULES), GENERAL SPECIFICATION FOR |
ASTM A 800/A800M : 2014 : REDLINE | Standard Practice for Steel Casting, Austenitic Alloy, Estimating Ferrite Content Thereof |
SAE AMS 5629H : 2016 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, RINGS, AND EXTRUSIONS, 13CR - 8.0NI - 2.2MO - 1.1AL, VACUUM INDUCTION PLUS CONSUMABLE ELECTRODE MELTED, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5653 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 17CR - 12NI - 2.5MO (0.030 MAX C) (316L), SOLUTION HEAT TREATED |
SAE AMS 5595 : 2014 | STEEL, CORROSION RESISTANT, SHEET, STRIP, AND PLATE, 9.0MN - 20CR - 6.5NI - 0.28N, SOLUTION HEAT TREATED |
SAE AMS 5622 : 2013 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 16CR - 4.0NI - 0.30CB - 4.0CU, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE, CONSUMABLE ELECTRODE REMELTED |
SAE AMS5624F:1989(S2017) | Steel Bars, High Expansion 4.5Mn - 4.0Cr - 12.5Ni (0.50 - 0.60C) Cold Finished(STABILIZED Apr 2017) |
SAE AMS 5853 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS AND WIRE, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED 1800 DEGREES F (982 DEGREES C) SOLUTION TREATED AND WORK-STRENGTHENED, 160 KSI (1103 MPA) TENSILE STRENGTH |
API 5LD CHINESE : 2009 | SPECIFICATION FOR CRA CLAD OR LINED STEEL PIPE |
SAE AMS 5503 : 2015 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 17CR (SAE 51430) ANNEALED |
SAE AMS 5764 : 2014 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, EXTRUSIONS, AND RINGS 5.0MN - 22CR - 12.5NI - 2.2MO - 0.20CB - 0.30N - 0.20V SOLUTION HEAT TREATED |
SAE AMS 5674 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, WIRE 18CR - 11.5NI - 0.70 CB (SAE 30347) SOLUTION HEAT TREATED |
SAE AMS 5507 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, SHEET, STRIP, AND PLATE, 17CR - 13NI - 2.5MO (316L), SOLUTION HEAT TREATED |
SAE AMS 5350 : 2017 | STEEL, CORROSION AND MODERATE HEAT-RESISTANT, INVESTMENT CASTINGS, 12.5CR (410), HARDENED AND TEMPERED |
SAE AMS 5646 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 18CR - 11NI - 0.60CB(NB) (347), SOLUTION HEAT TREATED |
SAE AMS 5903 : 2006 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 18CR - 9.0NI (SAE 30302), COLD ROLLED, 1/4 HARD, 125 KSI (862 MPA) TENSILE STRENGTH |
SAE AMS 6521 : 1983 | STEEL SHEET, STRIP, AND PLATE, MARAGING - 18.5NI - 9.0CO - 4.9MO - 0.65TI - 0.10AL, CONSUMABLE ELECTRODE MELTED SOLUTION HEAT TREATED |
SAE AMS 5618 : 2017 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 17CR - 0.52MO (0.95 - 1.20C) (440C), CONSUMABLE ELECTRODE VACUUM MELTED |
AWS A5.9/A5.9M : 2012 | SPECIFICATION FOR BARE STAINLESS STEEL WELDING ELECTRODES AND RODS |
SAE AMS 5571J:2012(R2018) | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS TUBING, 18CR - 10.5NI - 0.70CB (NB) (347), SOLUTION HEAT TREATED |
SAE AMS 5901B:2008 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 18CR - 8NI (SAE 30301), SOLUTION HEAT TREATED |
SAE AMS 5558H : 2016 | STEEL, CORROSION AND HEAT-RESISTANT, WELDED TUBING 18CR - 10.5NI - 0.70CB (NB) (347) THIN WALL SOLUTION HEAT TREATED |
SAE AMS 5734 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, AND TUBING, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED, 1650 DEGREES F (899 DEGREES C) SOLUTION HEAT TREATED |
ASTM B 599 : 1992 : R2009 : EDT 1 | Standard Specification for Nickel-Iron-Chromium-Molybdenum-Columbium Stabilized Alloy (UNS N08700) Plate, Sheet, and Strip |
SAE AMS 5356 : 2016 | STEEL, CORROSION RESISTANT, INVESTMENT CASTINGS, 15CR - 4.6NI - 0.22CB - 2.8CU, SOLUTION AND PRECIPITATION HEAT TREATED (H1100), 130 KSI (896 MPA) TENSILE STRENGTH |
SAE AMS 5910 : 2012 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 19CR - 9.2NI (SAE 30304) COLD ROLLED, 125 KSI (862 MPA) TENSILE STRENGTH |
ASTM F 1376 : 1992 : R2012 | Standard Guide for Metallurgical Analysis for Gas Distribution System Components |
SAE AMS 5637 : 2012 | STEEL, CORROSION RESISTANT, BARS AND WIRE 18CR - 9.0NI (SAE 30302) SOLUTION HEAT TREATED, COLD DRAWN AND STRESS RELIEVED 125 KSI (862 MPA) TENSILE STRENGTH |
SAE AMS 5719 : 2012 | STEEL BARS, WIRE, FORGINGS, TUBING, RINGS, AND EXTRUSIONS, CORROSION-RESISTANT, 11.8CR - 2.5NI - 1.8MO - 0.33V (0.08 - 0.15C), ANNEALED, VACUUM ARC OR ELECTROSLAG REMELTED |
SAE AMS 5584 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, SEAMLESS AND WELDED HYDRAULIC TUBING, 17CR - 12NI - 1.5MO - 0.03C MAX, COLD DRAWN, 1/8 HARD TEMPER |
ASTM B 599 : 1992 : R2014 | Standard Specification for Nickel-Iron-Chromium-Molybdenum-Columbium Stabilized Alloy (UNS N08700) Plate, Sheet, and Strip |
ASTM B 599 : 1992 : R2003 : EDT 1 | Standard Specification for Nickel-Iron-Chromium-Molybdenum-Columbium Stabilized Alloy (UNS N08700) Plate, Sheet, and Strip |
SAE AMS 5643 : 2018 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, MECHANICAL TUBING, AND RINGS, 16CR - 4.0NI - 0.30CB (NB) - 4.0CU, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
ASTM E 1473 : 2016 : REDLINE | Standard Test Methods for Chemical Analysis of Nickel, Cobalt and High-Temperature Alloys |
SAE AS 7229 : 2013 | RIVETS, STEEL, CORROSION AND HEAT RESISTANT, 18CR - 10.5NI - 0.70(CB+TA), SOLUTION HEAT TREATED, PROCUREMENT SPECIFICATION FOR |
SAE AMS 5899 : 2013 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 17CR - 0.52MO (0.95 - 1.20C), POWDER METALLURGY PRODUCT, HOT ISOSTATICALLY PRESSED |
SAE AMS 5576 : 2010 | STEEL, CORROSION AND HEAT RESISTANT, WELDED TUBING - 18CR - 10.5NI - 0.40TI (SAE 30321) SOLUTION HEAT TREATED |
SAE AMS 5651 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 25CR - 20NI (SAE 30310), SOLUTION HEAT TREATED |
BS EN 62321-5:2014 | Determination of certain substances in electrotechnical products Cadmium, lead and chromium in polymers and electronics and cadmium and lead in metals by AAS, AFS, ICP-OES and ICP-MS |
SAE AMS 5344 : 2013 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 16CR - 4.1NI - 0.28CB - 3.2CU, HOMOGENIZATION, SOLUTION, AND PRECIPITATION HEAT TREATED (H900), 180 KSI (1241 MPA) TENSILE STRENGTH (17-4) |
SAE AMS 6526 : 2016 | STEEL, BARS, FORGINGS, TUBING, AND RINGS, 1.0CR - 7.5NI - 4.5CO - 1.0MO - 0.09V (0.29 - 0.34C), CONSUMABLE ELECTRODE VACUUM REMELTED, ANNEALED |
SAE AMS 5621 : 2015 | STEEL, CORROSION RESISTANT, BARS, WIRE, AND FORGINGS, 13CR (0.30-0.40C) (51420), ANNEALED |
SAE AMS 5636 : 2006 | STEEL, CORROSION-RESISTANT, BARS AND WIRE, 18CR - 9.0NI (SAE 30302), SOLUTION HEAT TREATED AND COLD DRAWN, 100 KSI (689 MPA) TENSILE STRENGTH |
SAE AMS 5782 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE, 20.5CR - 9.0NI - 0.50MO - 1.5W - 1.2CB - 0.20TI, VACUUM INDUCTION MELTED |
SAE AMS 5515 : 2013 | STEEL, CORROSION RESISTANT, SHEET, STRIP, AND PLATE, 18CR - 8.5NI (302), SOLUTION HEAT TREATED, HIGH DUCTILITY |
BS ISO 12891-2:2014 | Retrieval and analysis of surgical implants Analysis of retrieved surgical implants |
SAE AMS 5688 : 2012 | STEEL, CORROSION-RESISTANT, WIRE, 18CR - 9.0NI (SAE 30302), SPRING TEMPER |
SAE AS 7211 : 2012 | PIN, COTTER, STEEL, CORROSION AND HEAT RESISTANT UNS S32100 PROCUREMENT SPECIFICATION |
SAE AMS 5642 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, AND FORGINGS, 18CR - 10.5NI - 0.60CB, FREE-MACHINING, SOLUTION HEAT TREATED |
SAE AMS 5827 : 2000 | STEEL, CORROSION RESISTANT, COVERED WELDING ELECTRODES, 16.4Cr 4.8Ni 0.22 Cb 3.6Cu |
SAE AMS 5351 : 2017 | STEEL CASTINGS, SAND, CORROSION AND MODERATE HEAT RESISTANT, 13CR, NORMALIZED AND TEMPERED |
SAE AMS 5743 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, BARS AND FORGINGS 15.5CR - 4.5NI - 2.9MO - 0.10N SOLUTION HEAT TREATED, SUB-ZERO COOLED, EQUALIZED, AND OVER-TEMPERED |
SAE AMS 5821 : 2011 | STEEL, CORROSION-RESISTANT, WELDING WIRE 12CR (SAE 51410 MODIFIED) FERRITE CONTROL GRADE |
SAE AMS 5648 : 2016 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 17CR - 12NI - 2.5MO (316), SOLUTION HEAT TREATED |
SAE AMS 5938 : 2011 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 10CR - 12NI - 2MO - 1.45AL - 1.15TI, VACUUM INDUCTION PLUS VACUUM CONSUMABLE ELECTRODE MELTED, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5726 : 2015 | STEEL, CORROSION AND HEAT-RESISTANT, BARS AND WIRE, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, 1800 DEGREES F (982 DEGREES C) SOLUTION HEAT TREATED AND WORK-STRENGTHENED, CONSUMABLE ELECTRODE REMELTED, 200 KSI (1379 MPA) TENSILE STRENGTH CAPABILITY |
SAE AMS 6533 : 2015 | STEEL, WELDING WIRE 2.0CR - 10NI - 14CO - 1.0MO - (0.13 - 0.17C) VACUUM MELTED, ENVIRONMENT CONTROLLED PACKAGING |
SAE MA 7211 : 2012 | PINS, COTTER, STEEL, CORROSION AND HEAT RESISTANT UNS S32100, METRIC PROCUREMENT SPECIFICATION FOR |
SAE AMS 5680 : 2011 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE 18.5CR - 11NI - 0.40CB (NB) (SAE 30347) |
SAE AMS 5573 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS TUBING, 17CR - 12NI - 2.5MO (SAE 30316), SOLUTION HEAT TREATED |
SAE AMS 5611 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 12CR, FERRITE CONTROLLED, CONSUMABLE ELECTRODE MELTED |
SAE AMS 5604 J: 2018 | STEEL, CORROSION RESISTANT, SHEET, STRIP, AND PLATE, 16.5CR - 4.0NI - 4.0CU - 0.30CB, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5561 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, WELDED AND DRAWN OR SEAMLESS AND DRAWN TUBING, 9.0MN - 20CR - 6.5NI - 0.28N, HIGH-PRESSURE HYDRAULIC |
SAE AMS 5559 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, WELDED TUBING, 18CR - 10.5NI - 0.40TI (SAE 30321), THIN WALL, SOLUTION HEAT TREATED |
SAE AMS 5744 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, BARS AND FORGINGS, 15.5CR - 4.5NI - 2.9MO - 0.10N, HEAT TREATED, 170 KSI (1172 MPA) TENSILE STRENGTH |
SAE AMS 5732 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING AND RINGS, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED 1800 DEGREES F (982 DEGREES C), SOLUTION AND PRECIPITATION HEAT TREATED |
SAE AMS 5656F : 2015 | STEEL, CORROSION RESISTANT, BARS, WIRE, FORGINGS, EXTRUSIONS, AND RINGS, 9.0MN - 20CR - 6.5NI - 0.27N, SOLUTION HEAT TREATED |
SAE AMS 5354 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, INVESTMENT CASTINGS, 13CR - 2.0NI - 3.0W, HARDENED AND TEMPERED TO 32 - 38 HRC |
AWS A5.35/A5.35M : 2015 | SPECIFICATION FOR COVERED ELECTRODES FOR UNDERWATER WET SHIELDED METAL ARC WELDING |
SAE AMS 5672 : 1981(S2017) | STEEL WIRE, CORROSION RESISTANT, 11.8CR - 8.5NI - 0.30(CB + TA) - 1.1TI - 2.0CU, PRECIPITATION HARDENABLE, SPRING TEMPER |
AWS A5.22/A5.22M : 2012 | SPECIFICATION FOR STAINLESS STEEL FLUX CORED AND METAL CORED WELDING ELECTRODES AND RODS |
SAE AMS 5564 : 2013 | STEEL, CORROSION RESISTANT, TUBING 19CR - 10NI (SAE 30304) HIGH-PRESSURE HYDRAULIC, WELDED PLUS ULTRASONICALLY TESTED OR SEAMLESS COLD DRAWN, ONE EIGHTH - HARD TEMPER |
SAE AMS 5857 : 2013 | STEEL, CORROSION-RESISTANT, BARS AND WIRE, 19CR - 10NI (304), HIGH YIELD STRENGTH, SOLUTION HEAT TREATED AND COLD WORKED |
SAE AMS 5913 : 2014 | STEEL, CORROSION-RESISTANT, SHEET AND STRIP, 19CR - 9.2NI (SAE 30304), COLD ROLLED, FULL HARD, 185 KSI (1276 MPA) TENSILE STRENGTH |
SAE AMS 5510S : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, SHEET, STRIP AND PLATE, 18CR - 10.5NI - 0.40TI (SAE 30321) SOLUTION HEAT TREATED |
SAE AMS 6518 : 1987 | STEEL SHEET, STRIP, AND PLATE, MARAGING, 19NI - 3.0MO - 1.4TI - 0.10AL DOUBLE VACUUM MELTED, SOLUTION HEAT TREATED |
SAE AMS 5745 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, BARS AND FORGINGS 16.5CR - 4.5NI - 2.9MO - 0.10N EQUALIZED AND OVER-TEMPERED |
SAE AMS 5347 : 2014 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 15CR - 4.6NI - 0.22CB (NB) - 2.8CU, SOLUTION AND PRECIPITATION HEAT TREATED (H1000), 150 KSI (1034 MPA) TENSILE STRENGTH (15-5) |
SAE AMS 5512 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, SHEET, STRIP, AND PLATE, 18CR - 10.5NI - 0.80CB (SAE 30347), SOLUTION HEAT TREATED |
ASTM B 599 : 1992 : R1997 | Standard Specification for Nickel-Iron-Chromium-Molybdenum-Columbium Stabilized Alloy (UNS N08700) Plate, Sheet, and Strip |
SAE AMS 5716 : 2016 | IRON-NICKEL ALLOY, HEAT RESISTANT, BARS, WIRE, FORGINGS, AND RINGS, 44FE - 18.5CR - 35.5NI - 1.1SI, SOLUTION HEAT TREATED |
SAE AMS 5342 : 2014 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 16CR - 4.1NI - 0.28CB (NB) - 3.2CU, HOMOGENIZATION, SOLUTION, AND PRECIPITATION HEAT TREATED (H1100), 130 KSI (896 MPA) TENSILE STRENGTH (17-4) |
SAE AMS 5931 : 2012 | STEEL, BARS, WIRE, FORGINGS, EXTRUSIONS, TUBING, AND RINGS WEAR, GALLING, AND CORROSION RESISTANT - 5.0MN - 3.5SI - 16.5CR - 5.0NI - 0.14N - SOLUTION HEAT TREATED |
SAE MAM 5822 : 2000 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE 11.8CR - 2.8NI - 1.6CO - 1.8MO - 0.32V VACUUM INDUCTION MELTED |
SAE AMS 5804 : 2013 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE, 15CR - 25.5NI - 1.3MO - 2.2TI - 0.006B - 0.30V |
ASTM E 30 : 1989 | Test Methods for Chemical Analysis of Steel, Cast Iron, Open-Hearth Iron, and Wrought Iron (Withdrawn 1995) |
SAE AMS 5525 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, SHEET, STRIP, AND PLATE 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, 1800 DEGREE F (982 DEGREE C) SOLUTION HEAT TREATED |
SAE AMS 5700G : 2018 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, FORGINGS, AND RINGS, 13.5CR - 13.5NI - 0.35MO - 2.2W, ANNEALED |
ASTM E 352 : 2013-05 | TEST METHODS FOR CHEMICAL ANALYSIS OF TOOL STEELS AND OTHER SIMILAR MEDIUM-AND HIGH-ALLOY STEELS |
ASTM F 561 : 2013 | Standard Practice for Retrieval and Analysis of Medical Devices, and Associated Tissues and Fluids |
ASME PV CODE 2C : 2017 | BOILER AND PRESSURE VESSEL CODE - MATERIALS - SPECIFICATIONS FOR WELDING RODS, ELECTRODES, AND FILLER METALS |
SAE AMS 5620 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, AND FORGINGS, 13CR (0.30 - 0.40C) (SAE 51420F, 51420FSE), FREE-MACHINING GRADE |
SAE AMS 5911 : 2014 | STEEL, CORROSION-RESISTANT, SHEET AND STRIP, 19CR - 9.2NI (SAE 30304) COLD ROLLED, 1/2 HARD, 150 KSI (1034 MPA) TENSILE STRENGTH |
SAE AMS 5358 : 2017 | STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT, 18CR - 9NI, SOLUTION HEAT TREATED |
SAE AMS 5508 : 2014 | STEEL, CORROSION AND HEAT RESISTANT, SHEET, STRIP, AND PLATE, 13CR - 2.0NI - 3.0W, ANNEALED |
SAE AMS 5500 : 2002 | STEEL, CORROSION-RESISTANT, LAMINATED, SHEET SURFACE BONDED |
SAE AMS 5578 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, WELDED TUBING, 12CR - 8.5NI - 0.30CB - 1.1TI - 2.0CU, VACUUM INDUCTION PLUS CONSUMABLE ELECTRODE VACUUM MELTED, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5557 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, SEAMLESS OR WELDED HYDRAULIC TUBING, 18.5CR - 10.5NI - 0.40TI (SAE 30321), SOLUTION HEAT TREATED |
SAE AMS 5412 : 2012R(2018) | STEEL CASTINGS, VACUUM MELTED, VACUUM CAST, INVESTMENT, CORROSION RESISTANT 13CR - 8.0NI - 2.2MO - 1.1AI (195,000 PSI (1344 MPA) TENSILE STRENGTH (CONDITION H1000) HOMOGENIZED, SOLUTION, AND PRECIPITATION HEAT TREATED |
SAE AMS 5568H : 2017 | STEEL, CORROSION AND HEAT RESISTANT, WELDED TUBING, 17CR - 7.1NI - 1.1AL, SOLUTION HEAT TREATED, PRECIPITATION-HARDENABLE |
SAE AMS 6512 H : 2017 | STEEL, MARAGING, BARS, FORGINGS, TUBING, AND RINGS 18NI - 7.8CO - 4.9MO - 0.40TI - 0.10AL CONSUMABLE ELECTRODE VACUUM MELTED, ANNEALED |
ASTM F 1376 : 1992 : R2005 | Standard Guide for Metallurgical Analysis for Gas Distribution System Components |
SAE AMS 5930 : 2017 | STEEL, CORROSION-RESISTANT, BARS AND FORGINGS 13.0CR - 2.5NI - 5.5CO - 2.0MO - 0.60V (0.05 - 0.09C) VACUUM INDUCTION PLUS VACUUM CONSUMABLE ELECTRODE MELTED |
SAE AMS 5824F : 2017 | STEEL, CORROSION-RESISTANT, WELDING WIRE 17CR - 7.1NI - 1.0AL |
SAE AMS 5907 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, SHEET, STRIP, AND PLATE, 17CR - 12NI - 2.5MO (SAE 30316), COLD ROLLED, 1/4 HARD, 125 KSI (862 MPA) TENSILE STRENGTH |
SAE AMS 6515 : 2012 | STEEL, MARAGING, BARS, FORGINGS, TUBING, AND RINGS 18.5NI - 12.0CO - 4.9MO - 1.40TI - 0.10AL DOUBLE VACUUM MELTED, ANNEALED |
SAE AMS 5363 : 2017 | STEEL CASTINGS, SAND AND CENTRIFUGAL, CORROSION AND HEAT RESISTANT, 18.5CR - 10.5NI - 0.90 (CB+TA), SOLUTION HEAT TREATED |
SAE AMS 5937 : 2012 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 12CR - 11NI - 2MO - 1.5AL - 0.3TI, VACUUM INDUCTION PLUS VACUUM CONSUMABLE ELECTRODE MELTED, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 6465 : 2000(S2017) | WIRE, STEEL WELDING, 2.0CR - 10NI - 8.0CO - 1.0MO - 0.02AL - 0.06V (0.10 - 0.14C) (HY-180), VACUUM MELTED, ENVIRONMENT CONTROLLED PACKAGING |
SAE AMS 5652J : 2016 | STEEL, CORROSION AND HEAT RESISTANT, BARS, WIRE, FORGINGS, MECHANICAL TUBING, AND RINGS 25CR - 20NI - 2.0SI (314) SOLUTION HEAT TREATED |
SAE AMS 5360 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, INVESTMENT CASTINGS, 17CR - 13NI - 1.9MO, SOLUTION HEAT TREATED |
SAE AMS 5514 : 2012 | STEEL, CORROSION RESISTANT, SHEET, STRIP, AND PLATE 18CR - 11.5NI (SAE 30305) SOLUTION HEAT TREATED |
SAE AMS 5343 : 2014 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 16CR - 4.1NI - 0.28CB (NB) - 3.2CU, HOMOGENIZATION, SOLUTION, AND PRECIPITATION HEAT TREATED (H1000), 150 KSI (1034 MPA) TENSILE STRENGTH (17-4) |
SAE AMS 5567 : 2015 | STEEL, CORROSION RESISTANT, SEAMLESS OR WELDED HYDRAULIC TUBING, 19CR - 10NI (304), SOLUTION HEAT TREATED |
SAE AS 7210 : 2012 | PINS, COTTER, STEEL, CORROSION RESISTANT UNS S30200 PROCUREMENT SPECIFICATION FOR |
SAE AMS 5823 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE 11.8CR - 2.8NI - 1.6CO - 1.8MO - 0.32V |
SAE AMS 6520E : 2016 | STEEL, MARAGING, SHEET, STRIP, AND PLATE, 18NI - 7.8CO - 4.9MO - 0.40TI - 0.10AL, CONSUMABLE ELECTRODE MELTED, SOLUTION HEAT TREATED |
SAE AMS 5934 : 2016 | STEEL, EXTRA HIGH TOUGHNESS, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, RINGS, AND EXTRUSIONS, 13CR - 8.0NI - 2.2MO - 1.1AL, VACUUM INDUCTION PLUS CONSUMABLE ELECTRODE MELTED, SOLUTION HEAT TREATED, PRECIPITATION-HARDENABLE |
SAE AMS 5877 : 2012 | IRON ALLOY, CORROSION AND HEAT-RESISTANT, BARS, FORGINGS, AND RINGS, 29FE - 22CR - 21NI - 18.5CO - 3.2MO - 2.8W - 0.78TA - 0.30AL - 0.05LA - 0.20N, SOLUTION HEAT TREATED |
SAE AMS 5803 : 2015 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE 16.4CR - 4.8NI - 0.22CB (NB) - 3.6CU CONSUMABLE ELECTRODE OR VACUUM INDUCTION MELTED |
SAE AMS 6466 : 2017 | STEEL, CORROSION-RESISTANT, WELDING WIRE, 5.2CR - 0.55MO |
SAE AMS 5511 : 2013 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 19CR - 9.5NI (304L), SOLUTION HEAT TREATED |
SAE AMS 5529 : 2012 | STEEL, CORROSION RESISTANT, SHEET AND STRIP, 17CR - 7.1NI - 1.1AL, SOLUTION HEAT TREATED AND COLD ROLLED, PRECIPITATION HARDENABLE, 0.0015 TO 0.100 INCH (0.038 TO 2.54 MM) NOMINAL THICKNESS |
SAE AMS5640V:2016 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 18CR - 9.0NI, FREE MACHINING |
SAE AMS 5630 : 2013 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 17CR - 0.52MO (0.95 - 1.20C) (440C) |
ASTM F 2281 : 2004 | Standard Specification for Stainless Steel and Nickel Alloy Bolts, Hex Cap Screws, and Studs, for Heat Resistance and High Temperature Applications |
SAE AMS 5641 : 2016 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS, 18.5CR - 10NI - 0.22SE (303SE), FREE-MACHINING; SWAGING OR UPSETTING SOLUTION HEAT TREATED |
SAE AMS 5649 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, AND FORGINGS, 18CR - 13NI - 2.1MO, FREE MACHINING, SOLUTION HEAT TREATED |
SAE AMS 5528 : 2012 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 17CR - 7.1NI - 1.1AL, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5549H:1987(S2017) | STEEL, CORROSION AND HEAT RESISTANT, PLATE 15.5CR - 4.5NI - 2.9MO - 0.10N SOLUTION HEAT TREATED |
SAE AMS 5678 : 2013 | STEEL, CORROSION RESISTANT, WIRE, 17CR - 7.1NI - 1.1AL, COLD DRAWN, PRECIPITATION-HARDENABLE |
SAE AMS 5518 : 2014 | STEEL, CORROSION RESISTANT, SHEET AND STRIP 18CR - 8NI COLD ROLLED, 150 KSI (1034 MPA) TENSILE STRENGTH |
SAE AMS 5565L : 2013 | STEEL, CORROSION RESISTANT, WELDED TUBING, 19CR - 9.5NI (304), SOLUTION HEAT TREATED |
SAE AMS 5574 : 2013 | STEEL, CORROSION AND HEAT RESISTANT, SEAMLESS TUBING, 23CR - 13.5NI (SAE 30309S) SOLUTION HEAT TREATED |
SAE AMS 5762 : 2016 | STEEL, CORROSION RESISTANT, BARS, WIRE, AND FORGINGS, 5.8MN - 17CR - 5.8NI - 2.0CU - 0.26S, FREE MACHINING, SOLUTION HEAT TREATED |
SAE AMS 5905 : 2012 | STEEL, CORROSION-RESISTANT, SHEET AND STRIP, 18CR - 9.0NI (SAE 30302), COLD ROLLED, 3/4 HARD, 175 KSI (1207 MPA) TENSILE STRENGTH |
SAE AMS5341:2012(S2017) | STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT, 19.5CR - 10.5NI - 0.25S (TYPE 303), SOLUTION HEAT TREATED |
SAE AMS 5955 : 2016 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS 10CR - 12NI - 2MO - 1.45AL - 1.15TI VACUUM INDUCTION PLUS VACUUM CONSUMABLE ELECTRODE MELTED SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5501 : 2002 | STEEL, CORROSION RESISTANT, SHEET, STRIP, AND FOIL, 19CR - 9.5NI (304), COLD ROLLED, 125 KSI (862 MPA) TENSILE STRENGTH |
SAE MA 4035 : 2012 | RINGS, RETAINING - SPIRAL WOUND, UNIFORM SECTION CORROSION RESISTANT, PROCUREMENT SPECIFICATION FOR, METRIC |
SAE AMS 6478 : 2001 | STEEL, BARS AND FORGINGS - 3.1CR - 11.5NI - 13.5CO - 1.2MO (0.21 - 0.25C) VACUUM MELTED, ANNEALED HEAT TREATABLE TO 290 KSI (1999 MPA) TENSILE STRENGTH |
ASTM A 781/A781M : 2018-02 | SPECIFICATION FOR CASTINGS, STEEL AND ALLOY, COMMON REQUIREMENTS, FOR GENERAL INDUSTRIAL USE |
ASTM E 350 : 2012-09 | TEST METHODS FOR CHEMICAL ANALYSIS OF CARBON STEEL, LOW-ALLOY STEEL, SILICON ELECTRICAL STEEL, INGOT IRON, AND WROUGHT IRON |
SAE AMS 5731 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED, 1800 DEGREES F (982 DEGREES C) SOLUTION HEAT TREATED |
SAE AMS 7445 : 2017 | BALLS, STEEL, CORROSION-RESISTANT 17CR ANNEALED |
SAE AMS 5524 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, SHEET, STRIP AND PLATE 18CR - 13NI - 2.5MO (SAE 30316) SOLUTION HEAT TREATED |
SAE AS 5685 : 2015 | STEEL, CORROSION RESISTANT, SAFETY WIRE, 18CR-11.5NI (UNS S30500), SOLUTION HEAT TREATED, COLD FINISHED |
SAE AMS 5738 : 2013 | STEEL, CORROSION-RESISTANT, BARS AND WIRE, 18CR - 9NI (SAE 30303F), FREE MACHINING, HIGH YIELD STRENGTH, SOLUTION HEAT TREATED AND COLD WORKED |
SAE AMS 5614 : 2013 | STEEL, CORROSION AND HEAT RESISTANT, BARS, WIRE, AND FORGINGS 12CR - 0.50MO, ANNEALED |
SAE AMS 5627 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 17CR (SAE 51430), ANNEALED |
SAE AMS 5932 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, FORGINGS AND TUBING 14.5CR - 2.3NI - 12.5CO - 4.0MO - 0.60V - 0.03CB(NB), CARBURIZING, PREMIUM AIRCRAFT-QUALITY, DOUBLE VACUUM MELTED |
SAE AMS 5867B : 2010(R2015) | STEEL, CORROSION AND HEAT RESISTANT, FORGINGS, 12.5CR (410), ENHANCED FRACTURE TOUGHNESS, ANNEALED |
SAE AMS 2431 : 2018 | PEENING MEDIA, GENERAL REQUIREMENTS |
SAE AMS 5547 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, SHEET AND STRIP, 15.5CR - 4.5NI - 2.9MO - 0.10N, SOLUTION HEAT TREATED |
SAE AMS 5340 : 2018 | STEEL, CORROSION RESISTANT, INVESTMENT CASTINGS, 14CR - 4.25NI - 2.25MO - 0.25CB - 3.25CU, HOMOGENIZATION AND SOLUTION HEAT TREATED |
SAE AMS 5749 : 2014 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, AND TUBING 14.5CR - 4.0MO - 1.2V (1.10-1.20C) PREMIUM QUALITY FOR BEARING APPLICATIONS, DOUBLE VACUUM MELTED |
SAE AMS 5689 : 2018 | STEEL, CORROSION AND HEAT RESISTANT, WIRE 18CR - 10.5NI - 0.40TI (321) SOLUTION HEAT TREATED |
SAE AMS 5810 : 2015 | STEEL, CORROSION AND HEAT RESISTANT, FLAT WIRE, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, 1800 DEGREES F (982 DEGREES C) SOLUTION TREATED, COLD DRAWN OR COLD ROLLED AND AGED, CONSUMABLE ELECTRODE REMELTED |
NASM24149:2001 | STUDS, WELDING, AND ARC SHIELDS (FERRULES), GENERAL SPECIFICATION FOR |
13/30242622 DC : 0 | BS ISO 12891-2 - RETRIEVAL AND ANALYSIS OF SURGICAL IMPLANTS - PART 2: ANALYSIS OF RETRIEVED SURGICAL IMPLANTS |
SAE AMS 5348 : 2017 | STEEL CASTINGS, TUBULAR, CENTRIFUGAL, CORROSION RESISTANT, 15CR - 4.6NI - 0.22 (CB+TA) - 2.8CU, SOLUTION HEAT TREATED |
SAE AMS 5912 : 2014 | STEEL, CORROSION-RESISTANT, SHEET AND STRIP, 19CR - 9.2NI (SAE 30304), COLD ROLLED, 3/4 HARD, 175 KSI (1207 MPA) TENSILE STRENGTH |
SAE AMS 5746 : 2012 | ALLOY, CORROSION AND HEAT RESISTANT, BARS AND FORGINGS - 15CR - 45NI - 4.1MO - 4.1W - 3.0TI - 1.0AL - 31FE (D979) CONSUMABLE ELECTRODE VACUUM MELTED, SOLUTION AND PRECIPITATION HEAT TREATED |
SAE AMS 5361G : 2013(S 2019) | STEEL CASTINGS, SAND AND CENTRIFUGAL, CORROSION AND HEAT RESISTANT, 18.5CR - 13.5NI - 2.1MO, SOLUTION HEAT TREATED |
SAE AMS5337E : 2017 | STEEL, MARAGING, INVESTMENT CASTINGS, 18.5NI - 9.0CO - 5.0MO - 0.70TI - 0.12AL, VACUUM MELTED, HOMOGENIZED, OVERAGED, AND SOLUTION HEAT TREATED |
SAE AMS 5556 : 2016 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS OR WELDED HYDRAULIC TUBING 18CR - 11NI - 0.70CB (347) SOLUTION HEAT TREATED |
SAE AMS 5368 : 2012 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS 15CR - 4.0NI - 2.3MO - 0.09N SOLUTION HEAT TREATED |
SAE AMS 5513 : 2015 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 19CR - 9.2NI (SAE 30304), SOLUTION HEAT TREATED |
SAE AMS 5817 : 2011 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE, 13CR - 2.0NI - 3.0W |
SAE AMS 5692 : 2011 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE, 19CR - 12.5NI - 2.5MO |
ASTM E 2209 : 2013 : REDLINE | Standard Test Method for Analysis of High Manganese Steel by Spark Atomic Emission Spectrometry |
SAE AMS5659S : 2016 | Steel, Corrosion-Resistant, Bars, Wire, Forgings, Rings, and Extrusions 15Cr - 4.5Ni - 0.30Cb (Nb) - 3.5Cu<br> |
SAE AMS 6519 : 2014 | STEEL, MARAGING, BARS, FORGINGS, TUBING, AND RINGS 19NI - 3.0MO - 1.4TI - 0.10AL PREMIUM AIRCRAFT QUALITY DOUBLE VACUUM MELTED, ANNEALED |
SAE AMS 5812 : 2015 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE, 15CR - 7.1NI - 2.4MO - 1.0AL, VACUUM INDUCTION MELTED |
SAE AMS 5774 : 2015 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE 16.5CR - 4.5NI - 2.9MO - 0.10N |
SAE AMS 6516 : 2017 | STEEL, BARS AND FORGINGS 1CR - 10NI - 7CO - 2MO - 1.3W - 0.1V - (0.28 - 0.32C) VACUUM INDUCTION MELTED, VACUUM ARC REMELTED, NORMALIZED AND ANNEALED PRECIPITATION HARDENABLE |
SAE AMS 5825 : 2017 | STEEL, CORROSION-RESISTANT, WELDING WIRE 16.4CR - 4.8NI - 0.22CB(NB) - 3.6CU |
SAE AMS 5516 : 2012 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 18CR - 9.0NI (SAE 30302), SOLUTION HEAT TREATED |
SAE AMS 5904 : 2012 | STEEL, CORROSION-RESISTANT, SHEET AND STRIP, 18CR - 9.0NI (SAE 30302), COLD ROLLED, 1/2 HARD, 150 KSI (1034 MPA) TENSILE STRENGTH |
SAE AMS 2280 : 2012 | TRACE ELEMENT CONTROL, NICKEL ALLOY CASTINGS |
SAE AMS 5776 : 2008(R2015) | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE, 12.5CR (SAE 51410) |
SAE AMS 5818 : 2013 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE, 9.0MN - 20CR - 6.2NI - 0.20N |
SAE AMS 5769 : 2014 | ALLOY, CORROSION AND HEAT-RESISTANT, BARS, FORGINGS, AND RINGS, 21CR - 20NI - 20CO - 3.0MO - 2.5W - 1.0(CB+TA) - 0.15N - 32FE SOLUTION HEAT TREATED |
SAE AMS 5563 : 2012 | STEEL, CORROSION RESISTANT, SEAMLESS OR WELDED TUBING, 19CR - 9.5NI (SAE 30304), COLD DRAWN, 1/4 HARD TEMPER |
SAE AMS 5591 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, TUBING, SEAMLESS, 12.5CR (SAE 51410), ANNEALED |
SAE AMS 5690 : 2015 | STEEL, CORROSION AND HEAT RESISTANT, WIRE, 17CR - 12NI - 2.5MO (316), SOLUTION HEAT TREATED |
SAE AS 7472 : 2015 | BOLTS AND SCREWS, STEEL, CORROSION RESISTANT 125000 PSI TENSILE STRENGTH ROLL THREADED |
SAE AMS 6543 : 2016 | STEEL, BARS AND FORGINGS, 2.0CR - 10NI - 8.0CO - 1.0MO (0.10 - 0.14C) (HY-180), DOUBLE VACUUM MELTED, SOLUTION HEAT TREATED, MARAGE HARDENABLE |
SAE AMS 5763E : 2016 | STEEL, CORROSION RESISTANT BARS, FORGINGS, TUBING, AND RINGS, 15CR - 6.5NI - 0.75MO - 0.50CB (NB) - 1.5CU, SOLUTION HEAT TREATED |
SAE ARP 1313 : 2014 | DETERMINATION OF TRACE ELEMENTS IN HIGH TEMPERATURE ALLOYS |
SAE AMS 5929 : 2014 | STEEL, CORROSION-RESISTANT, BARS AND FORGINGS, 11.5CR -10NI - 1.0AL - 0.5TI - 1.0CU - 1.0W, VACUUM INDUCTION PLUS VACUUM CONSUMABLE ELECTRODE MELTED SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5645 : 2016 | STEEL, CORROSION AND HEAT RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 18CR - 10NI - 0.40TI (321), SOLUTION HEAT TREATED |
SAE AMS 5933 : 1999 | STEEL, CORROSION RESISTANT BARS AND FORGINGS, 12.5CR - 1.0NI - 15.5CO - 2.0MO, VACUUM INDUCTION PLUS, VACUUM CONSUMABLE ELECTRODE REMELTED |
SAE AMS 5352 : 2015 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 17CR - 0.55MO (0.95 - 1.20C), ANNEALED |
API 5LD : 2017 | CRA CLAD OR LINED STEEL PIPE |
ASTM F 2281 : 2004 : R2017 | Standard Specification for Stainless Steel and Nickel Alloy Bolts, Hex Cap Screws, and Studs, for Heat Resistance and High Temperature Applications |
SAE AMS 5862M:2017 | STEEL, CORROSION-RESISTANT, SHEET, STRIP, AND PLATE, 15CR - 4.5NI - 0.30CB (NB) - 3.5CU, CONSUMABLE ELECTRODE REMELTED, SOLUTION HEAT TREATED, PRECIPITATION-HARDENABLE |
ASTM E 38 : 1985 | Methods for Chemical Analysis of Nickel-Chromium and Nickel-Chromium-Iron Alloys (Withdrawn 1989) |
SAE AMS 5366 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, INVESTMENT CASTING 25CR - 20NI (CK-20) AS-CAST |
SAE AMS 5357 : 2017 | STEEL, CORROSION RESISTANT, INVESTMENT CASTINGS, 15CR - 4.6NI - 0.22CB - 2.8CU, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
ISO 12891-2:2014 | Retrieval and analysis of surgical implants Part 2: Analysis of retrieved surgical implants |
SAE AMS 5822 : 2011 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE, 11.8CR - 2.8NI - 1.6CO - 1.8MO - 0.32V, VACUUM INDUCTION MELTED |
SAE AMS 5805 : 2012 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.004B - 0.30V, VACUUM INDUCTION MELTED, ENVIRONMENT CONTROLLED PACKAGING |
ASTM B 471 : 1993 | Specification for UNS NO8020, UNS N08026, and UNS NO8024 Nickel Alloy Spring Wire (Withdrawn 1999) |
API 5LD REDLINE : 2009 | SPECIFICATION FOR CRA CLAD OR LINED STEEL PIPE |
SAE AMS 6522 : 2016 | STEEL PLATE 2.0CR - 10NI - 14CO - 1.0MO (0.13 - 0.17C) VACUUM MELTED, NORMALIZED, AND OVERAGED |
SAE AMS 5863E : 2009(R2015) | STEEL, CORROSION RESISTANT, SHEET, STRIP, AND PLATE, 15CR - 6.5NI - 0.75MO - 0.60CB - 1.5CU, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5600 : 2007 | STEEL, CORROSION-RESISTANT, SHEET, LAMINATED, EDGE BONDED |
SAE AMS 5922 : 2015 | STEEL, CORROSION-RESISTANT, BARS, AND FORGINGS, 10CR - 5.5NI - 14CO - 2MO - 1W (0.19-0.23C), VACUUM INDUCTION MELTED, VACUUM ARC REMELTED, NORMALIZED, ANNEALED |
SAE AMS 5560 : 2016 | STEEL, CORROSION RESISTANT, SEAMLESS TUBING, 19CR - 10NI (304), SOLUTION HEAT TREATED |
SAE AMS 5895 : 2015 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, CONSUMABLE ELECTRODE MELTED, 1750 DEGREES F (954 DEGREES C) SOLUTION HEAT TREATED, WELDING GRADE, PRECIPITATION HARDENABLE |
SAE AMS 5639 : 2017 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, MECHANICAL TUBING, AND RINGS, 19CR - 10NI, SOLUTION HEAT TREATED |
NFL 06 835 : 2007 | AEROSPACE SERIES - METALLIC PARTS - INDUCEMENT COMPRESSIVE SURFACE STRESSES - STEEL SHOT CUT WIRE (SPHERICAL) |
SAE AMS 5923 : 2013 | STEEL, CORROSION-RESISTANT, BARS, WIRE, AND FORGINGS,17CR - 0.52MO (0.95 - 1.20C) (SAE 51440C), FOR BEARING APPLICATIONS |
SAE AMS 5570 : 2013 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS TUBING 18CR - 11NI - 0.40TI (321), SOLUTION HEAT TREATED |
SAE AMS 5735 : 1974 | STEEL BARS, FORGINGS, TUBING, AND RINGS, CORROSION AND HEAT RESISTANT, 15CR - 26NI - 1. 3MO - 2.1TI - 0.30V, 1800 DEGREES F (982.2 DEGREES C) SOLUTION AND PRECIPITATION HEAT TREATED |
SAE AMS 5519 : 2014 | STEEL, CORROSION RESISTANT, SHEET AND STRIP, 18CR - 8NI (SAE 30301) COLD ROLLED, 185 KSI (1276 MPA) TENSILE STRENGTH |
SAE AMS 5647 : 2017 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, MECHANICAL TUBING, AND RINGS, 19CR - 9.5NI, SOLUTION HEAT TREATED |
SAE AMS 5625 : 2018 | STEEL BARS, HIGH EXPANSION, 9.5NI - 5.5MN (0.55 - 0.65C), COLD FINISHED |
SAE AMS 5790 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE 20CR - 10NI - 0.75CB, HIGH FERRITE GRADE |
SAE AMS 5858 : 2015 | STEEL, CORROSION AND HEAT RESISTANT, SHEET, STRIP, AND PLATE, 15CR - 25.5NI - 1.2MO - 2.1TI - 0.006B - 0.30V, MULTIPLE MELTED, 1800 DEGREES F (982 DEGREES C) SOLUTION HEAT TREATED, WELDING GRADE, PRECIPITATION HARDENABLE |
SAE AMS 5364 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, INVESTMENT CASTINGS, 19.5CR - 10.5NI - 0.65CB (CF-8C), SOLUTION HEAT TREATED |
SAE AMS 5840 : 2010 | STEEL, CORROSION AND HEAT RESISTANT, WELDING WIRE, 13CR - 8.0NI - 2.3MO - 1.1AL, VACUUM MELTED |
IFI 153 : 2003 | STAINLESS STEEL WIRE AND RODS FOR MECHANICAL FASTENERS |
ASTM F 2281 : 2004 : R2012 | Standard Specification for Stainless Steel and Nickel Alloy Bolts, Hex Cap Screws, and Studs, for Heat Resistance and High Temperature Applications |
SAE AS 7228 : 2015 | RIVETS, STEEL, CORROSION RESISTANT 18CR-9NI, SOLUTION HEAT TREATED, PROCUREMENT SPECIFICATION FOR |
SAE AMS 6514 : 2017 | STEEL, MARAGING, BARS, FORGINGS, TUBING, AND RINGS 18.5NI - 9.0CO - 4.9MO - 0.65TI - 0.10AL CONSUMABLE ELECTRODE VACUUM MELTED, ANNEALED |
SAE AMS 5572 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS TUBING, 25CR - 20NI (SAE 30310S), SOLUTION HEAT TREATED |
SAE AMS 5859 : 2012 | STEEL, CORROSION RESISTANT, SHEET, STRIP, AND PLATE, 15CR - 6.5NI - 0.75MO - 0.30CB - 1.5CU, CONSUMABLE ELECTRODE MELTED, SOLUTION HEAT TREATED, PRECIPITATION HARDENABLE |
SAE AMS 5826 : 2017 | STEEL, CORROSION AND HEAT-RESISTANT, WELDING WIRE 15CR - 5.1NI - 0.30CB(NB) - 3.2CU |
SAE AMS 5616 : 2014 | STEEL, CORROSION AND HEAT-RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS 13CR - 2.0NI - 3.0W ANNEALED |
SAE AMS 5896 : 2015 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS OR WELDED HYDRAULIC TUBING, 18.5CR - 10.5NI - 0.55TI (321), SOLUTION HEAT TREATED AND COLD DRAWN, 1/8 HARD TEMPER |
SAE AMS 5655 : 2016 | STEEL, CORROSION AND HEAT RESISTANT, BARS, WIRE, AND FORGINGS 12.5CR - 0.75NI - 1.0MO - 1.0W - 0.24V (0.20-0.25C) HARDENED AND TEMPERED |
SAE AMS 6525 : 2016 | STEEL, BARS, FORGINGS, TUBING, AND RINGS, 0.75CR - 9.0NI - 4.5CO - 1.0MO - 0.09V (0.17 - 0.23C), CONSUMABLE ELECTRODE VACUUM MELTED |
SAE AMS5554G:2016 | STEEL, CORROSION AND HEAT-RESISTANT, SEAMLESS TUBING, 16.5CR - 4.5NI - 2.9MO - 0.10N, ANNEALED |
AWS A5.4/A5.4M : 2012 | SPECIFICATION FOR STAINLESS STEEL ELECTRODES FOR SHIELDED METAL ARC WELDING |
I.S. EN 62321-5:2014 | DETERMINATION OF CERTAIN SUBSTANCES IN ELECTROTECHNICAL PRODUCTS - PART 5: CADMIUM, LEAD AND CHROMIUM IN POLYMERS AND ELECTRONICS AND CADMIUM AND LEAD IN METALS BY AAS, AFS, ICP-OES AND ICP-MS |
AWS A5.9 : 93(R1999) | BARE STAINLESS STEEL WELDING ELECTRODES AND RODS, SPECIFICATION FOR |
ASTM E 354 : 2014 : REDLINE | Standard Test Methods for Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron, Nickel, and Cobalt Alloys |
SAE AMS 5926 : 2016 | STEEL, CORROSION-RESISTANT, BARS, WIRE, TUBING, AND FORGINGS 15.5CR - 1.5SI - 0.3MO - 0.1N (0.45 - 0.60C) FOR BEARING APPLICATIONS |
SAE AMS 5353E : 2007(R2015) | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 16CR - 1.8NI - 0.08N, AS CAST |
API TR 17TR8 : 2018 | HIGH-PRESSURE HIGH-TEMPERATURE DESIGN GUIDELINES |
SAE AMS 5400 : 2014 | STEEL, CORROSION-RESISTANT, INVESTMENT CASTINGS, 15CR - 4.6NI - 0.22CB - 2.8CU, SOLUTION AND PRECIPITATION HEAT TREATED (H935), 170 KSI (1172 MPA) TENSILE STRENGTH |
SAE AMS 5585 : 2016 | ALLOY, CORROSION AND HEAT RESISTANT, WELDED TUBING, 32FE - 21CR - 20NI - 20CO - 3MO - 2.5W - 1.0CB (NB) - 0.15N, SOLUTION HEAT TREATED |
SAE AMS 5718E : 2016 | STEEL, BARS, FORGINGS, TUBING, AND RINGS, CORROSION RESISTANT, 11.8CR - 2.5NI - 1.8MO - 0.33V (0.08 - 0.15C), ANNEALED |
SAE AMS 5686 : 2012 | STEEL, CORROSION RESISTANT, RIVET WIRE, 18CR - 11.5NI (SAE 30305), SOLUTION HEAT TREATED |
SAE AMS 5613 : 2013 | STEEL, CORROSION AND HEAT RESISTANT, BARS, WIRE, FORGINGS, TUBING, AND RINGS 12.5CR (SAE 51410) ANNEALED |
SAE AMS 5638 : 2015 | STEEL, CORROSION-RESISTANT, BARS AND FORGINGS, 0.14S - 18CR - 9.5NI - 0.50MO - 0.80AL (303MA), FREE-MACHINING; SWAGING OR UPSETTING, SOLUTION HEAT TREATED |
SAE AMS 5592 : 2013 | IRON-NICKEL ALLOY, CORROSION AND HEAT-RESISTANT, SHEET, STRIP, AND PLATE, 44FE - 18.5CR - 35NI - 1.15SI, SOLUTION HEAT TREATED |
SAE AMS 5339 : 2017 | STEEL, MARAGING, INVESTMENT CASTINGS, 17NI - 10CO - 4.6MO - 0.30TI - 0.06AL, VACUUM MELTED, HOMOGENIZED, OVERAGED AND SOLUTION HEAT TREATED |
SAE AMS 5628 : 2015 | STEEL, CORROSION-RESISTANT, BARS, WIRE, FORGINGS, AND TUBING, 16CR - 2.5NI (SAE 51431) |
ASTM F 3184 : 2016 | Standard Specification for Additive Manufacturing Stainless Steel Alloy (UNS S31603) with Powder Bed Fusion |
SAE AMS 5548 : 2012 | STEEL, CORROSION AND HEAT-RESISTANT, SHEET AND STRIP, 16.5CR - 4.5NI - 2.9MO - 0.10N, 1850 TO 1975 DEGREES F (1010 TO 1079 DEGREES C) ANNEALED |
ASTM F 621 : 2012 : R2017 | Standard Specification for Stainless Steel Forgings for Surgical Implants |
ASTM F 621 : 2012 | Standard Specification for Stainless Steel Forgings for Surgical Implants |
EN 62321-5:2014 | Determination of certain substances in electrotechnical products - Part 5: Cadmium, lead and chromium in polymers and electronics and cadmium and lead in metals by AAS, AFS, ICP-OES and ICP-MS |
ASTM E 50 : 2017 : REDLINE | Standard Practices for Apparatus, Reagents, and Safety Considerations for Chemical Analysis of Metals, Ores, and Related Materials |
ASTM E 350 : 2012-09 | TEST METHODS FOR CHEMICAL ANALYSIS OF CARBON STEEL, LOW-ALLOY STEEL, SILICON ELECTRICAL STEEL, INGOT IRON, AND WROUGHT IRON |
ASTM E 1601 : 2012 : REDLINE | Standard Practice for Conducting an Interlaboratory Study to Evaluate the Performance of an Analytical Method |
ISO 5725:1986 | Precision of test methods Determination of repeatability and reproducibility for a standard test method by inter-laboratory tests |
ASTM E 173 : 1993 | Practice for Conducting Interlaboratory Studies of Methods for Chemical Analysis of Metals (Withdrawn 1997) |
ASTM E 352 : 2013-05 | TEST METHODS FOR CHEMICAL ANALYSIS OF TOOL STEELS AND OTHER SIMILAR MEDIUM-AND HIGH-ALLOY STEELS |
ASTM E 354 : 2014 : REDLINE | Standard Test Methods for Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron, Nickel, and Cobalt Alloys |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.