ASTM C 1176/C1176M : 2013 : REDLINE
Superseded
A superseded Standard is one, which is fully replaced by another Standard, which is a new edition of the same Standard.
View Superseded by
Standard Practice for Making Roller-Compacted Concrete in Cylinder Molds Using a Vibrating Table
22-10-2020
English
15-12-2013
CONTAINED IN VOL. 04.02, 2014 Defines procedures for making cylindrical test specimens from concrete when the standard procedures of rodding and internal vibration, as described in Practice C 31, are not practicable.
Committee |
C 09
|
DevelopmentNote |
Supersedes ASTM C 1176. (07/2008)
|
DocumentType |
Redline
|
Pages |
5
|
PublisherName |
American Society for Testing and Materials
|
Status |
Superseded
|
SupersededBy | |
Supersedes |
1.1This practice covers procedures for making cylindrical test specimens from concrete when the standard procedures of rodding and internal vibration, as described in Practice C31/C31M, are not practicable. This practice is applicable to freshly mixed concrete, prepared in the laboratory and the field, having a nominal maximum size aggregate of 50 mm [2 in.] or less. If the nominal maximum size aggregate is larger than 50 mm [2 in.], the practice is applicable only when performed on the fraction passing the 50-mm [2-in.] sieve with the larger aggregate being removed in accordance with Practice C172. This practice, intended for use in testing roller-compacted concrete, may be applicable to testing other types of concrete such as cement-treated aggregate and mixtures similar to soil-cement.
1.2Two methods are provided for making concrete cylinders using a vibrating table:
1.2.1Method A is a procedure for making test specimens in steel reusable molds attached to a vibrating table.
1.2.2Method B is a procedure for making test specimens in single-use plastic molds that have been inserted into a metal sleeve attached to a vibrating table.
1.3The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ACI 207.5R : 2011 | REPORT ON ROLLER-COMPACTED MASS CONCRETE |
ASTM C 39/C39M : 2018 : REDLINE | Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens |
ASTM C 1245/C1245M : 2012 : REDLINE | Standard Test Method for Determining Relative Bond Strength Between Hardened Roller Compacted Concrete Lifts (Point Load Test) |
ASTM C 470/C470M : 2015 : REDLINE | Standard Specification for Molds for Forming Concrete Test Cylinders Vertically |
ASTM C 192/C192M : 2016-04 | PRACTICE FOR MAKING AND CURING CONCRETE TEST SPECIMENS IN THE LABORATORY |
ASTM C 496/C496M : 2017 : REDLINE | Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens |
ASTM E 11 : 2017 : REDLINE | Standard Specification for Woven Wire Test Sieve Cloth and Test Sieves |
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.